XLPE Insulation Compound

Silane Cross-linked Polyethylene Insulation Compound for Cables

This cable compound delivers excellent extrusion performance and processing adaptability, making it well-suited for high-speed production lines. It ensures a smooth surface finish and stable dimensional control even under high-speed extrusion. Its wide processing window allows for easy handling with low screw torque and energy consumption. As a result, it enables high production efficiency and faster line speeds without compromising product quality.

No.	Ítem de Prueba	Unidad	Test Value of YJWG-10
1	Resistencia a la Tracción	MPa	≥16.0
2	Alargamiento en la Ruptura	%	≥500
3	Test Temperature T Low Temperature Brittleness	℃ Failure Count	-76 ≤15/30
4	Air Heat Aging （135±2℃、168h） Tasa de Cambio de Resistencia a la Tracción Tasa de Cambio de Alargamiento en la Ruptura	% %	≤±20 ≤±20
5	Hot Set Test：200℃、0.2MPa、15min Alargamiento bajo Carga Deformación Permanente después del Enfriamiento	% %	≤175 ≤15
6	Dielectric Dissipation Factor 50Hz，20℃	–	≤1.0×10^-3
7	Relative Permittivity 50Hz，20℃	–	≤2.35
8	Resistividad Volumétrica a 20℃	Ω·m	≥1.0×10¹⁴
9	Resistencia Dieléctrica	MV/m	≥25
10	Carbon Black Content	%	Per customer requirement
11	Note: Black A compound or natural A compound (corresponding to natural B compound or black B compound) can be supplied per customer requirement.

Applicable to the insulation layer of overhead cables rated up to 10kV.

Productos Relacionados

Construyamos el Futuro

Por favor, proporcione los siguientes detalles para ayudar a nuestros representantes de ventas a comprender mejor sus necesidades y ponerse en contacto con usted lo antes posible.

XLPE Insulation Compound

Productos Relacionados

Productos relacionados

Cable ACS

Compuesto de cable LSZH

Material de Aluminio para Accesorios de Energía Eléctrica

Alambre de Cobre

Construyamos el Futuro